Team:Newcastle/problem

From 2010.igem.org

(Difference between revisions)
(Reasons cracks are bad)
(Reasons cracks are bad)
Line 15: Line 15:
Work in this area has already been started:
Work in this area has already been started:
-
[http://www.youtube.com/watch?v=PyBR3PDPa-c Bio-concrete] and a non-biological method of [http://ace-mrl.engin.umich.edu/|self healing concrete].
+
[http://www.youtube.com/watch?v=PyBR3PDPa-c Bio-concrete] and a non-biological method of [http://ace-mrl.engin.umich.edu/ self healing concrete].
Those projects mentioned above are different from ours because they only allow bacteria to repair cracks that form almost instantly after concrete sets, which are cracks formed in new buildings, whereas our Bacilla Filla can repair cracks that were formed in existing structures. This makes a lot of difference to the construction industry because it can halt the process of corrosion in steel reinforcements in existing structures. Also, our cells would die after a certain period of time after repairing the crack thus making Bacilla Filla environmentally friendly.
Those projects mentioned above are different from ours because they only allow bacteria to repair cracks that form almost instantly after concrete sets, which are cracks formed in new buildings, whereas our Bacilla Filla can repair cracks that were formed in existing structures. This makes a lot of difference to the construction industry because it can halt the process of corrosion in steel reinforcements in existing structures. Also, our cells would die after a certain period of time after repairing the crack thus making Bacilla Filla environmentally friendly.

Revision as of 21:10, 25 October 2010

iGEM Homepage Newcastle University BacillaFilla Homepage Image Map

Contents

Problem

BacillaFilla repairing cracks in concrete

Concrete Background

Deena's concrete lecture provides some basic knowledge on concrete as well as questions from our presentation at iGEM UK Get Together.

Reasons cracks are bad

  1. Allow water to reach and corrode steel reinforcements;
  2. Weaken concrete structures;
  3. Difficult to repair.

Work in this area has already been started: [http://www.youtube.com/watch?v=PyBR3PDPa-c Bio-concrete] and a non-biological method of [http://ace-mrl.engin.umich.edu/ self healing concrete].

Those projects mentioned above are different from ours because they only allow bacteria to repair cracks that form almost instantly after concrete sets, which are cracks formed in new buildings, whereas our Bacilla Filla can repair cracks that were formed in existing structures. This makes a lot of difference to the construction industry because it can halt the process of corrosion in steel reinforcements in existing structures. Also, our cells would die after a certain period of time after repairing the crack thus making Bacilla Filla environmentally friendly.

How our project is helpful

  1. Reduces corrosion rate of the steel reinforcements;
  2. Reduces the need to demolish and replace existing concrete structures;
  3. Reduces cement production;
  4. Reduces carbon dioxide emission from cement production;
  5. Reduces consumption of energy resources.

How our project is novel

  1. Our project focuses not only on newly set concrete structures, but also existing ones.
  2. All the cells will produce calcium carbonate which has similar properties to concrete
  3. Filamentous Bacillus subtilis cells have similar properties to the synthetic fibres used in fibre-reinforced concrete, and thereby act as reinforcements within the crack.
  4. Getting the BacillaFilla to produce levans glue which will hold everything together and will fill up the crack
  5. Environmental kill switch
  6. We are working with a well known strain: Bacillus subtilis 168 (previous work required specific stains)

5th August 2010

Concrete Splitting Test

On the 5th of August, the whole team went down to the Structures Lab of Cassie Building that houses the School of Civil Engineering and Geosciences, to do tensile splitting test on a concrete cylinder. We tried to understand the problems of crack formation on the concrete structures and how our project BacillaFilla will help.

More photos

Dr. Colin Davie showing steel reinforcements of concrete
How cracks form in bridges
Concrete in tensile strength testing machine
Concrete cylinder cracked into two
Teaching properties of concrete
Tensile strength testing machine
Dr. Colin Davie carrying cracked concrete
Concrete in tensile strength testing machine
Structures lab assistant, Billie explaining how concrete cracked

Materials used to mix concrete

Coarse aggregates
Fine aggregates
Cement


References

  1. Neville A. (2008) Properties of Concrete. 4th Edition, London, Pearson Education Limited.